Abstract In the bentonite industry - exploration and beneficiation - ore quality control has been traditionally carried out using the swelling parameter, denominating those that swell as naturally sodium bentonites and those that do not as naturally non-sodium bentonites. However, the properties of the bentonites can vary due to the quantity and cationic type of montmorillonite. The variation in those properties cannot always be predicted, because there is still no consolidated and convenient method for clays mineralogical quantification. A quantification via PXRD using the Rietveld method is only reliable when all the crystalline structures of the mineral phases are known. This is not the case for bentonites, since the montmorillonite shows turbostratic disorder that leads to extremely wide and asymmetric non-basal reflections that are not considered in the available structural models. Thus, in this work, is generate a calibrated hkl model for a Brazilian montmorillonite applying the combined Rietveld-Le Bail-Internal Standard method developed by Paz et al. (2018). The study concluded that the combined method is a good choice for the mineralogical quantification of the bentonites, handling turbostratic disorder of montmorillonite, since the develop hkl phase model showed good results in mixtures with >50% montmorillonite content (greater precision and reproducibility).

Ultramarine pigments were successful synthesized from zeolite A obtained from kaolin waste. This waste has been used as an excellent source of silicon and aluminum for zeolite synthesis because of its high kaolinite concentrations and low contents of other accessory minerals. The cost is naturally less than the industrialized product. Color additives (Sulfur and Sodium Carbonate) were mixed with different proportions of zeolite A and further calcined for 5 h at 500 °C. They were characterized by XRD and XRF in addition to visual classification by color and shade. These products show colors from blue to green at different shades, both influenced by the amount of additives and cooling rate after calcination. Thus, a different quantity of the same additives in the same zeolitic matrix provides an increase in the color intensity. Cooling rate after calcination induces the color change which is substantially important in the pigments production.

Basic sodalite was successfully synthesized by hydrothermal method using kaolin waste as source of Aluminum and Silicon. This waste is mainly composed by kaolinite and is produced in large amount by kaolin processing industries for paper coating from the Amazon region. Initially, the waste has been calcined at 700 ºC for 2 h and then reacted with the following solutions: Na2CO3 and mixture of Na2CO3 + NaOH to 150 ºC with autogenous pressure for 24 h. The raw materials and transformed materials were characterized by XRD, FTIR and SEM. In both studied media, well-crystallized, basic sodalite was the only phase synthesized, while in the literature usually a mixture of zeolites is obtained.